PERFORMANCES OF CRACK RESISTANCE OF THE TUBE STEEL 20 WITH STRUCTURE OF THE NATURAL FERRIT-MARTENSITIC COMPOSITE MATERIAL
Abstract
Results of experimental researches about influence of structure of trumpet steel 20 on characteristics of resistance to destruction are resulted. It is shown, that with the purpose of achievement of the greatest possible characteristics of resistance it is necessary for destruction to determine dependence of these characteristics at a variation of a volume fraction of a strengthening phase and the attitude l/d.
About the Authors
V.V. MULCHIN
Don State Technical University.
Russian Federation
Russian Federation
D.S. LOMONOSOV
Don State Technical University.
Russian Federation
Russian Federation
References
1. Иванова В.С. Физика и химия обработки материалов/В.С.Иванова, Л.М. Устинов. 1969. №2. -С.114-121.
2. Сорокин В.Л. Применение электропотенциального метода для определения характера развития трещины/В.Л.Сорокин, В.Ф.З-митрук, Г.В.Шербединский//Заводская лаборатория. 1981, т.47, №12. -С. 60-62.
3. Браун У. Испытания высокопрочных металлических материалов на вязкость разрушения при плоской деформации/У.Браун, Дж.Сроули.-М.: МИР, 1972. -248 с.
4. Келли А. Высокопрочные материалы/А.Келли. -М.: МИР, 1976. -261 с.
5. Таран А.В. Природа разрушения высокопрочных материалов/А.В.Таран.//МиТОМ, 1971, №1. -С.55-61.
Review
For citations:
MULCHIN V., LOMONOSOV D. PERFORMANCES OF CRACK RESISTANCE OF THE TUBE STEEL 20 WITH STRUCTURE OF THE NATURAL FERRIT-MARTENSITIC COMPOSITE MATERIAL. Vestnik of Don State Technical University. 2007;7(4):480-484. (In Russ.)
Views:
275
Email this article 